FeCrAl 0Cr23Al5 Alloy Resistance Wire
20.0~45.0 USD
| Min. Order: | 50 Kilogram |
|---|---|
| Payment Terms: | L/C, D/P, D/A, T/T, WU |
| Supply Ability: | 2 Tons per Month |
| Place of Origin: | Beijing |
Company Profile
| Location: | Beijing, China (Mainland) |
|---|---|
| Business Type: | Manufacturer |
| Main Products: | Resistance Wire, Resistance Furnace Wire, Nichrome Resistance Wire, Kanthal A Wire, Heat Resistance Wire |
Product Detail
| Means of Transport: | Ocean, Air, Land |
|---|---|
| Resistance Heating Wire: | Resistance Wire |
| Production Capacity: | 2 Tons per Month |
| Packing: | Standard Export Package |
| Delivery Date: | 3-30days |
Product Description
FeCrAl 0Cr23Al5 Alloy Resistance Heating Wire
The FeCrAl 0Cr23Al5 Alloy Resistance Heating Wire is a ferritic iron-chromium-aluminium alloy (FeCrAl alloy) which is used at temperatures up to 1250°C. It is used in fast response elements for ceramic glass top hobs and quartz tube heaters. FeCrAl 0Cr23Al5 Alloy Resistance Heating Wire is widely used in household lectrical appliance, heating elements, mechanical manufacturing and other industrial fields.
FeCrAl Resistance Heating Wire has high resistance, low temperature coefficient of electric resistance, high operating temperature, and good corrosion resistance under high temperature, especially under the atmosphere containing sulfides. FeCrAl Resistance Heating Wire possesses good oxidation and heat resistance.It iscreep-resistant over a wide range of temperature. FeCrAl Resistance heating Wire has advantages such as lower raw-material cost, superior oxidation resistance, lower density, and lower thermal expansion coefficient than the nickel base super-alloys.
FeCrAl Resistance heating Wire has less hot strength than nickel alloys but much higher melting point and lower price. After being heated the Resistance Wire's plasticity becomes bad, easy brittleness, not to be easy to weld. However, If can be reasonably used, also be a kind of ideal electric heating material. FeCrAl Resistance Wire has excellent oxidation properties at 800-1300° C because of the formation of a highly protective Al2O3 scale.
Chemical Composition (%) and Properties
FeCrAl 0Cr23Al5 Alloy Resistance Wire | ||
Main Chemical Composition | Cr | 20.5-23.5 |
Al | 4.2-5.3 | |
Fe | Rest | |
Mn | ≤0.7 | |
Max Continuous Service Temp.of Element °C | 1250 | |
Density g/cm³ | 7.25 | |
Resistivity Ω m²/m | 1.35±0.06 | |
Temp.Coefficient of Resistance | 14.5 | |
Melting point | °C | 1500 |
Tensile strength | Mpa | 637-784 |
Elongation % | >12 | |
Variation of area | % | 65-75 |
Bending frequency | >5 | |
Hardness | 200-260 | |
Micrographic Structure | F | |
Magnetic Property | Magnetic | |
Wire Specification
Wire | CNS 2962-1984 | Diameter:0.05mm-10.0mm, 0.002 Inch to 0.3937 Inch |
Manufacture Process
The manufacture started with producing ingot by advanced vacuum melting process. The wire production includes forging, rolling, annealing and drawing. From the ingot to the final thin wire, manufacture process is operated with high standard quality control system. There will be quality test for each batch of product, such as test to diameter tolerance, content, hardness, etc.
Packing Process & Transportation
Packaging: Seal up, with plastic inside and wooden case or carton outside; or according to the customer's requirements.
Transportation: By air or By sea