Material: | ZIRCONIA |
Size: | 98*10/12/14/16/18/20/22/25mm |
System: | 98mm, 95mm, 92*75mm |
Type: | ST Colored Zirconia Block |
Translucency: | 42% |
Strength: | 1100MPa |
Production Capacity: | 30000 pieces per month |
Packing: | 1 piece/box |
Delivery Date: | one week |
Features:
·Safe high quality raw material
·Excellent aesthetic and strength
·Preferred and most common colored material used for posterior restoration
Translucency: 42%
Strength: 1100MPa
Shade: A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4
System: 98mm, 95mm, 92*75mm
Thickness: 10mm, 12mm, 14mm, 16mm, 18mm, 20mm, 22mm, 25mm, 30mm
Indications:
·Veneer
·Inlay & Onlay
·Inner crown
·Full contour of anterior
·Full contour of posterior
·Implant full contour
·Full contour bridge (≤3 units)
·Full contour bridge (≥4 units)
·Inner crown bridge (≤3 units)
·Inner crown bridge (≥4 units)
·Implant abutment
Density after sintering | ≥6.09g/cm3 |
Fracture Toughness | ≥5.0Mpa.m1/2 |
Flexural strength after sintering | (Hv10) 1250 |
Sintering Temperature | 1530 °C |
ZrO2+HfO2 +Y2O3 | ≥99% |
Y2O3 | 4.5%-6.0% |
AI203 | < 0.15% |
Other Oxides | <0.15% |