ZG-P-6687/ZG-I-5002,Children Shoes Sole PU Resin Manufacturer,PU Resin For Men Casual Shoes
Children Shoes Sole PU Resin Manufacturer
PU Resin For Men Casual Shoes
Q/ZHTY 01—2010
Characteristic: High hardness, medium and high density good resilience
Application: Applicable to the production of low-speed type
Typical properties of PU Resin
Name of products | Appearance | Viscosity(Pa·s/50℃) | Density(g/cm3/40℃) | Package(kg) |
ZG-P-6687 | Milky,liquid, no foreign materia | 6.0±2.0 | ---- | 18 |
ZG-I-5002 | Transparentliquid, no foreignmaterial | 1.5±0.5 | ---- | 20 |
Catalysts and auxiliary agents
ZG-P-6687/ZG-AC-2/water =18kg/220-320g/30-60g/
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Molding conditions & physical properties
Reactivity | Technical index | Test item | Reference physicalproperties |
Reference ratioP+C/I | 100/110~112 | Molded density of sole(g/cm3) | 0.5-0.7 |
Material temperature(℃) | material:45-50 B material:38-42 | Hardness (type C) | 80~90 |
Cream time(s) | 6~9 | Tensile strength(MPa) | 3.5~4.5 |
Rise time(s) | Elongation(％) | 250~350 | |
Metal mold temperature(℃) | 50~60 | NBS abrasion resistance(％) | |
Demould time(min) | 3.0~7.0 | Free foam density(g/cm3) | 0.30-0.40 |
Sports Shoes Sole PU Resin
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.