ZG-P-5090/ZG-I-5320,Sole PU Resin For Business Shoes,Isocyanate Prepolymer
Sole PU Resin For Business Shoes
Isocyanate Prepolymer
High-hardness and medium and high-density PU Resin for shoe sole of woman high-heeled shoes
Characteristic: High hardness, medium and high density
Application: Applicable to the production of female high-heeled shoes
Typical properties of PU Resin
Name of products | Appearance | Viscosity(Pa·s/50℃) | Density(g/cm3/40℃) | Package(kg) |
ZG-P-5090 | White or pale yellow, liquid, no foreign material | 0.40-0.80 | 1.16-1.20 | 18 |
ZG-I-5320 | Transparent liquid, no foreign material | 0.10-0.30 | 1.18-1.20 | 20 |
Reference shipments ratio: A/B=25/28 (barrel)
Catalysts and auxiliary agents:
ZG-P-5090/ZG-AC-2/water=18kg/220g/40-80g
Low Density High Hardness Sole Pu Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Molding conditions & physical properties:
Reactivity | Technical index | Test item | Reference physical properties |
Reference ratioP+C/I | 100/118-122 | Molded density of sole(g/cm3) | 0.55~0.75 |
Using temperature(℃) | material: 45-50; B material:38-42 | Hardness (type A) | 75~85 |
Cream time(s) | 6~9 | Tensile strength(MPa) | 3.5~4.5 |
Rise time(s) | 30~45 | Elongation(％) | 250~350 |
Metal mold temperature(℃) | 45~55 | NBS abrasion resistance(％) | ≥10% |
Demould time(min) | 5.0~7.0 | Free foam density(g/cm3) | 0.28~0.35 |
mm)Folding endurance (room temperature)(40,000 gap length mm) | ＜8 |
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.