ZG - P -3650S/ZG-I-9823
| Min. Order: | 3 Ton |
|---|---|
| Payment Terms: | L/C, T/T |
| Supply Ability: | 1000000ton |
| Place of Origin: | Zhejiang |
Company Profile
| Location: | Taizhou, Zhejiang, China (Mainland) |
|---|---|
| Business Type: | Manufacturer |
Product Detail
| Brand Name: | Headspring |
|---|---|
| Production Capacity: | 1000000ton |
| Delivery Date: | 14days |
Product Description
ZG-P-3650S/ZG-I-9823,Low Hardness Sole PU Resin Supplier,Low Density Low Hardness Sole Pu
Low Hardness Sole PU Resin Supplier
Low Density Low Hardness Sole Pu
PU Resin for Auto Parts
Characteristic: Medium and low hardness, medium density
Characteristic: Applicable to the production of related auto parts.
Typical properties of PU Resin
Name of products | Appearance | Viscosity(Pa·s/50℃) | Density(g/cm3/40℃) | Package(kg) |
ZG-P-3650S | White or pale yellow, liquid, no foreign material | 0.50-0.90 | 1.16-1.20 | 18 |
ZG-I-9823 | Transparent liquid, no foreign material | 0.05-0.20 | 1.18-1.20 | 20 |
Reference shipments ratio: A/B=28/25 (barrel)
Catalysts and auxiliary agents:
ZG-P-3650S/ZG-AC-2/water =18kg/280g/80g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Poly ISO For Shoe Sole Molding conditions & physical properties:
Reactivity | Technical index | Test item | Referencephysical properties |
Reference ratioP+C/I | 100/87-89 | Molded density of sole(g/cm3) | 0.35~0.42 |
Using temperature(℃) | material:45-50;B material:38-42 | Hardness (type A) | 60~70 |
Cream time(s) | 6~9 | Tensile strength(MPa) | 3.5~4.5 |
Rise time(s) | 30~45 | Elongation(％) | 350~450 |
Metal mold temperature(℃) | 45~55 | NBS abrasion resistance(％) | ≥10% |
Demould time(min) | 4.0~6.0 | Free foam density(g/cm3) | 0.24~0.28 |
mm)Folding endurance (room temperature)(40,000 gap length mm) | ＜8 |
Low Hardness Sole PU Resin Supplier
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.