Molde | Standards | Deposit Composition | Mechanical property | ||||||||
AWS | C | Si | Mn | Cr | Ni | Mo | S.P | Rm(MPa) | A5(%) | ||
LA307 | E307T0-1 E307T0-4 | 0.09 | 0.6 | 4.25 | 19.47 | 1.15 | 1.3 | ≤0.03 | 613 | 46 | |
LA308L | E308LT1-1 E308LT1-4 | 0.028 | 0.69 | 1.26 | 20.27 | 10.82 | ≤0.03 | 553 | 43 | ||
LA309L | E309LT0-1 E309LT0-4 | 0.030 | 0.59 | 1.21 | 23.11 | 13.56 | 0.04 | ≤0.03 | 557 | 42 | |
LA309Mo | E309LoMoT0-1 E309LoMot0-4 | 0.027 | 0.71 | 1.17 | 23.68 | 14.86 | 2.49 | ≤0.03 | 541 | 35 | |
LA316L | E316LT0-1 E316LT0-4 | 0.029 | 0.57 | 1.33 | 18.35 | 12.49 | 2.42 | ≤0.03 | 516 | 44 | |
ER308LSI 309 316L 317L 347 410 welding wire | |||||||||||
Brand | (mm) | Shielding Gas | Chemical Composition of Deposited Metal(%) | ||||||||
C | Si | Mn | P | S | Cr | Ni | Mo | Cu | |||
ER308 | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.08 | 0.3-0.65 | 1.0-2.5 | 0.03 | 0.03 | 19.5-22.0 | 9.0 -11.0 | 0.75 | 0.75 |
ER308L | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.03 | 0.3-0.65 | 1.0-2.5 | 0.03 | 0.03 | 19.5-22.0 | 9.0 -11.0 | 0.75 | 0.75 |
ER308LSI | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.03 | 0.65-1.0 | 1.0-2.5 | 0.03 | 0.03 | 19.5-22.0 | 9.0 -11.0 | 0.75 | 0.75 |
ER309 | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.12 | 0.3-0.65 | 1.0-2.5 | 0.03 | 0.03 | 23.0-25.0 | 12.0 -14.0 | 0.75 | 0.75 |
ER309L | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.03 | 0.3-0.65 | 1.0-2.5 | 0.03 | 0.03 | 23.0-25.0 | 12.0 -14.0 | 0.75 | 0.75 |
ER310 | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.08-0.15 | 03-0.65 | 1.0-2.5 | 0.03 | 0.03 | 25.0-28.0 | 20.0 -22.5 | 0.75 | 0.75 |
ER312 | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.15 | 0.3-0.62 | 1.0-2.5 | 0.03 | 0.03 | 28.0-32.0 | 8.0 -10.5 | 0.75 | 0.75 |
ER316 | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.08 | 0.3-0.65 | 1.0-2.5 | 0.03 | 0.03 | 18.0-20.0 | 11.0 -14.0 | 2.0-3.0 | 0.75 |
ER316L | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.03 | 0.3-0.65 | 1.0-2.5 | 0.03 | 0.03 | 18.0-20.0 | 11.0 -14.0 | 2.0-3.0 | 0.75 |
ER316LSI | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.03 | 0.65-1.0 | 1.0-2.5 | 0.03 | 0.03 | 18.0-20.0 | 11.4 -14.0 | 2.0-3.0 | 0.75 |
ER410 | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.12 | 0.5 | 0.6 | 0.03 | 0.03 | 11.5-13.5 | 0.6 | 0.75 | 0.75 |
ER430 | 0.6-4.0 | Ar+0.5 -2%CO2 | 0.1 | 0.5 | 0.6 | 0.03 | 0.03 | 15.5-17.0 | 0.6 | 0.75 | 0.75 |
Chemical composition of deposited metal
C | Si | Mn | Cr | Ni | S | P | Mo | Cu |
≤0.08 | 0.30~0.65 | 1.00~2.50 | 19.00~22.00 | 9.0~11.0 | ≤0.03 | ≤0.03 | ≤0.75 | ≤0.75 |
Mechanical propeties of deposited metal
Tensile strength | Specific elongation |
MPa | % |
570~610 | 36~42 |