polycarboxylate superplasticizer(40% 50%) high range water reduce pce flake
| Min. Order: | 1 Ton |
|---|---|
| Payment Terms: | L/C, T/T |
| Supply Ability: | 30000 |
| Place of Origin: | Hubei |
Company Profile
| Location: | Wuhan, Hubei, China (Mainland) |
|---|---|
| Business Type: | Manufacturer |
Product Detail
| Brand Name: | DICT |
|---|---|
| Production Capacity: | 30000 |
| Packing: | 25KG |
Product Description
POYLYCARBOXYLATE SUPERPLASTICIZER CONCRETE ADMIXTURE
PRODUCT FEATURES
Technical Characteristics | |||
Test items | Performance Indicators | Test Results | |
Formaldehyde Content % | ≤0.05 | 0.003 | |
Cement Paste Fluidity (mm) | ≥240 | 273 | |
Sodium content % | ≤5.0 | 1.1 | |
Chloride ion content % | ≤0.2 | 0.13 | |
Alkali content(Na2O+0.658 K2O) % | ≥5.0 | 1.8 | |
Gas Content % | Mixed with None-Freezing Proofing Concrete | ≥3.0 | 4.5 |
Mixed with Antifreeze Concrete | ≥4.5 | ||
Slump Retention (mm) | 30min | ≥180 | 195 |
60min | ≥150 | 175 | |
Water Reduction Ratio % | ≥20 | 25 | |
Atmospheric Bleeding Ratio % | ≤20 | 0 | |
Pressure Bleeding Ratio % | ≤90 | 45 | |
Compressive strength Ratio,% | 3d | ≥130 | 172 |
7d | ≥125 | 166 | |
28d | ≥120 | 153 | |
Steel Corrosion Effect | None | None | |
Shrinkage Ratio % | ≤135 | 97 | |
Relative Durability Index % 200 Times | ≥80 | 85 | |
Note: Above all are calculated based on 20% of solids content. The dosage is 1.0% of gelled material.
METHOD OF USE
Ÿ Under normal circumstance, it calculated based on 40% of solids content, dosage is 0.3%-0.75% of gelled material. The recommended dosage is 0.5%.
Ÿ Please test and find out the best dosage rate before using it.
ADVANTAGES
Low dosage 0.5~1.5% (by gelled material weight)
High water reduction up to 21~25%.
Wide adaptability, can used in all kinds of concrete projects and cement products.
Meet the international standards environmental protection rules: ISO14000.