Nimonic 901/UNS N09901/2.4662/Alloy 901 Forged Forging Steel Extrusion Presses Container Liners Inner Intermediate Liner
| Min. Order: | 100 Kilogram |
|---|---|
| Payment Terms: | L/C, T/T |
| Supply Ability: | 1000 tons |
| Place of Origin: | Jiangsu |
Company Profile
| Location: | Wuxi, Jiangsu, China (Mainland) |
|---|---|
| Business Type: | Manufacturer |
Product Detail
| Model No.: | df |
|---|---|
| Means of Transport: | Ocean, Air |
| Brand Name: | liangyi |
| material grade of extrusion liners: | 901 |
| size of forged extrusion liner: | as per the drawing |
| origin of forged extrusion liners: | china |
| delivery time: | 30 days |
| packing: | plywooden case |
| certificate: | API |
| export to country: | american european |
| Production Capacity: | 1000 tons |
| Packing: | plywooden cases |
| Delivery Date: | 60 days |
Product Description
We are professional Nimonic 901(UNS N09901,2.4662,Alloy 901)Forged Forging Steel Extrusion Presses Container Liners Inner Intermediate Liner from china
Alloy % Ni Cu Al
Fe Ti Co Mn S C Si P Cr Mo B nimonic 901 Min.
40.0 2.35 11.0 5.0 0.01
Max. 45.0 0.50 0.35 Balance 3.10 1.0 1.0 0.03 0.10 0.60 0.03
14.0
7.0 0.02 nimonic 901 Physical properties:
Density 8.14 g/cm3 Melting point 1280-1345℃ nimonic 901 minimum mechanical properties in the room temperature:
Status Tensile strength Rm N/mm2 Yield strength
RP0.2N/mm2
Elongation
A5 %
nimonic 901 1034 689 12 Description A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.
Corrosion Resistance Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.
Workability
Hot Working Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.
Weldability Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before and aging.