Min. Order: | 10000 Kilogram |
---|---|
Trade Term: | FOB,CFR,CIF |
Payment Terms: | Paypal, L/C, T/T, WU |
Place of Origin: | Zhejiang |
Location: | Hangzhou, Zhejiang, China (Mainland) |
---|---|
Business Type: | Manufacturer, Trading Company |
Model No.: | XG/U7 |
---|---|
Means of Transport: | Ocean |
Application: | Industrial Lubricant |
Type: | Greases |
General Composition: | Base Oil |
Base oil: | High viscosity base oil |
Thickener: | Polyurea. |
Additives: | anti-oxidation , anti-rust,anti-corrosion, anti-wear, EP, etc |
NLGI-grade: | 2#,3#, |
Characters: | AW, EP |
Service temperature min. [°C: | -20 |
Service temperature max. [°C: | 200 |
Packaging: | pail, drum |
Company nature: | manufacturer |
Application: | bearings |
Packing: | 18 kg/ pail, 180 kg metal drum, adjustable according to customers' requirements. |
Delivery Date: | Shipped in 25 days after payment |
Overview
Base Oil | High viscosity base oil | This is multipurpose high temperature grease for motor and bearing protection. |
Thickener | Polyurea. | |
Additives | anti-oxidation , anti-rust,anti-corrosion, anti-wear, EP, etc. |
Product Introduction
Longer operation life;
With better high speed performance, for lubricating the bear with DN 500000mm·r/min long-time;
Excellent high temperature performance, meet the requirement of high temperature H type motor;
Great anti-water, anti-acid, anti-alkaline capacity;
With great lubricating capability, meet the requirements of small, middle, large and Super-huge type motors.
Applicable between -20℃ and +200℃, for lubrication of all kinds of bearings for big, middle, small type motor, especially suitable for H type motor, second-level and large motor with higher revolving rate; Or the motor under the conditions with acid gas, alkaline gas, vapor, etc.; also lubricating for the friction parts in the pumps, wind turbines under above conditions.
Typical Values
Item | Unit | Typical Values | Test Method | |
2# | 3# | |||
Worked cone penetration | 0.1mm | 265~295 | 220~250 | GB/T 269 |
Dropping Point | ℃ ≥ | 280 | 280 | GB/T 3498 |
Oil separation by steel mesh | 100℃, 24h % ≤ | 1.3 | 1.0 | SH/T 0324 |
Similar Viscosity | -10ºC,10s-1, Pa·s | 600 | 1000 | SH/T 0048 |
Evaporation | (99℃, 24h) % ≤ | 0.6 | 0.4 | GB/T 0337 |
Roll stability test (28℃,2h) | No adding water; change rate; Adding 10% water, change rate. 0.1mm | 9 | 9 | SH/T 0122 |
Corrosion | (T2 sheet copper, 100℃, 24h) ≤ | No green or black change | GB/T 7326 (Method B) |
-20℃~+200℃.