Austenite/ Martensite/ Ferrite Irregular Stainless Steel Powder for Sintering Parts
| Min. Order: | 1 Kilogram |
|---|---|
| Payment Terms: | L/C, T/T |
| Supply Ability: | 2500 TON PER YEAR |
| Place of Origin: | Hebei |
Company Profile
| Location: | Shijiazhuang, Hebei, China (Mainland) |
|---|---|
| Business Type: | Manufacturer |
Product Detail
| Model No.: | 005 |
|---|---|
| Production Capacity: | 2500 TON PER YEAR |
| Packing: | 25kg/iron barrel |
| Delivery Date: | 7-15 working days after received the deposit |
Product Description
Stainless Steel Powder for Sintering Parts
Product Introduction
We adopted the best refining process to make the ingredients matched and more uniform.
Compressibility,compactibility and green density can achieve the best
results in a stable condition on the basis of our rich experience in
mixing additives.
Technical Parameters
| Austenitic Stainless Steel | Ferritic Stainless Steel | Ferritc/Martensite Stainless Steel | |||||||
| 304L | 303L | 316L | 409LE | 434L | 410L | ||||
| Powder Properties | |||||||||
| Apparent Density, g/cm3 | 2.85 | 2.90 | 2.75 | 2.70 | 2.72 | 2.70 | |||
| Flow Rate, s/50g | 28 | 27 | 32 | 34 | 34 | 34 | |||
| Chemical Compositions | |||||||||
| C, % | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | |||
| Ni, % | 9.5 | 10.2 | 12.8 | ||||||
| Fe, % | Balance | Balance | Balance | Balance | Balance | Balance | |||
| Cr, % | 19 | 19.5 | 18 | 12 | 16.8 | 12.5 | |||
| Si, % | 0.9 | 0.9 | 0.8 | 0.8 | 0.8 | 0.8 | |||
| O, % | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | |||
| N, % | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | |||
| Mo, % | 2.5 | 1.0 | |||||||
| Nb, % | 0.5 | ||||||||
| Sieving (µm ) | |||||||||
| +150, % | 0.8 | 0.8 | 1 | 0.9 | 0.9 | 0.9 | |||
| -45, % | 43 | 40 | 41 | 45 | 42 | 42 | |||
| The Green Properties | |||||||||
| GD 600 MPa g/cm3 The Green Density with Lubricant | 6.45 | 6.4 | 6.5 | 6.45 | 6.45 | 6.45 | |||
| GS 600 MPa, Mpa The Green Strength with Lubricant | 7.5 | 7.1 | 8.5 | 14 | 12 | 13 | |||
| Lubricant = 1% Acrawax | |||||||||
| Sintering Temperature | 1150° C | 1250° C | 1150° C | 1250° C | 1150° C | 1250° C | 1250° C | 1250° C | 1250° C |
| Sintering Density, g/cm3 | 6.7 | 6.78 | 6.68 | 6.75 | 6.85 | 6.92 | 6.9 | 6.9 | 7.02 |
| Performance and Application Examples | - Excellent Corrosion Resistance - Non-Magnetic - Application is suitable for the production of locks and home appliance parts. | Free processing of Austenitic Stainless Steel | - Corrosion resistance is extremely high, especialy suitable for chlorine ion solution - Non-Magnetic - Often used in the production of stainless steel powder metallurgy parts in different areas, such as small gear, cam and linker | - Medium Corrosion Resistance - Ferromagnetic - Suitable for welding - Suitable for the production of automobile exhaust flage and hot exhaust gas oxygen sensor hubparts | - Medium Corrosion Resistance and higher than 400 series - Excellent magnetic property - Suitable for the production of automobile exhaust flange parts | - Medium Corrosion Resistance - Ferromagnetism - Suitable for the production of sensor circle parts of ABS system - Graphite can be added ( to increase hardness and abrasion performance) 410/420 Convert into Martensite Stainless Steel 410/420 | |||