C11000 - T2 Rolled Copper Foil Roll One Side Matte And One Side Shiny
| Place of Origin: | Guangdong |
|---|
Company Profile
| Location: | Shanghai, China (Mainland) |
|---|---|
| Business Type: | Manufacturer |
| Main Products: | RA Copper Foil |
Product Detail
| Model No.: | AIA-1 |
|---|
Product Description
C11000 - T2 Rolled Copper Foil Roll One Side Matte And One Side Shiny
Description :
Civen RA Copper Foil is rolled from pure copper ingots, the process including purifying copper ores, make into copper cathodes, ingoting, rolling, annealing, washing, testing, slitting and packing. Our copper ores are imported from South America, which were famous for their copper mining.
Applications:
(1) Flexible Copper Clad Laminate(FCCL)
(2) Fine Circuit FPC
(3) LED coated crystal thin film.
(4) Adhesion Tape
(5) Anti - Peel devices and so on
Normal Specification:
(1) Thickness: 0.012mm / 0.018mm / 0.035mm
(2) Width: 260mm / 520mm and so on .
Performances:
(1) High flexibility and extensibility
(2) Even and smooth surface
(3) Good fatigue resistance
(4) Strong antioxidant properties
(5) Cuts with scissors or paper cutter .
(6) Can be hammered, texturized or punched.
(7) Used for many outside or inside projects.
(8) There are many applications based on workability and beauty.
(9) Dead soft, very pliable .
Table 1 :
|
Item |
Unit |
Parameters |
|||||
|
12μm |
18μm |
25μm |
35μm |
70μm |
|||
|
Mass per unit(±5%) |
g/m² |
105 |
160 |
300 |
400 |
445 |
|
|
Cu+Ag |
% |
≥99.99 |
|||||
|
Temper |
|
H |
O,H |
O,H |
O,H |
O,H |
|
|
Surface roughness |
Ra |
μm |
0.13 |
0.12 |
0.1 |
0.08 |
0.08 |
|
Rz |
μm |
1.3 |
1.0 |
0.8 |
0.74 |
0.76 |
|
|
Tensile strength |
Normal Temp /23 |
N/mm² |
≥430 |
≥450 |
≥450 |
≥450 |
≥450 |
|
High Temp /220 |
N/mm² |
≥140 |
≥150 |
≥170 |
≥210 |
≥220 |
|
|
Elongation |
Normal Temp /23 |
% |
≥1.5 |
≥3.0 |
≥4.0 |
≥4.2 |
≥4.5 |
|
High Temp /220 |
% |
≥8 |
≥10 |
≥18 |
≥28 |
≥30 |
|
|
Fatigue Resistance (annealed) |
% |
65 |
65 |
65 |
65 |
65 |
|
|
Maximum resistivity |
Ωmm2/m |
0.0181 |
|||||
|
Electrical conductivity |
% |
≥98.3% |
|||||
|
Film and adhesive layers |
Instant Temp. 300/10s |
Film and adhesive paste after transient temperature without blistering delamination. |
|||||
|
Anti oxidation |
H.T.(200) |
Minute |
Won’t Change the Color within 60 minutes |
||||
|
Pinhole test results |
piece/ m² |
Pinhole area more than 0.5 mm²,0.005 piece/ m² |
|||||
Note:
1. Above figures based on the material with 0.05mm in thickness and 600mm in width.
2. Normally, Copper, cobalt and nickel is coated on the rough surface.
3. Testing method follows our company standard.
Table 3 :
Contact Us: