Junhetec JH-9382 water - base micro layer corrosion protection coating
| Place of Origin: | Guangdong |
|---|
Company Profile
| Location: | Changzhou, Jiangsu, China (Mainland) |
|---|---|
| Business Type: | Manufacturer |
| Main Products: | Zinc Flake Coating, Water Based Top Coat, Dip Spin Coating Machine |
Product Detail
| Model No.: | AIA-1 |
|---|
Product Description
Technical Data Sheet
1 Product Information
Trade Name: Zincover
Article/Model No.:JH-9382
2 Composition/information on ingredients
JH-9382 is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.
3 Coating Process
3.1 Mix Ratio
Pack A:16.0 kg
Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)
Pack C:0-50 g (according to different viscosity demand )
3.2
Before Mixture, Keep weighted A&B into the water bath at 25±2 , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.
3.3
Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35, startup refrigerating device to keep the barrel temperature constant at 35.
3.4
Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.
3.5
The coating should be filtrated by 100 mesh stainless steel screen before pouring into dip barrel.
v
3.6
Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.
3.7
Test Specific gravity,PH,Temperature,Viscosity of coating every 8 hours if operate continuously.
5 Technical data
|
No. |
Item |
Data |
|
1 |
PH |
3.8-5.2 |
|
2 |
Cr6+ |
≥25g/L |
|
3 |
Specific gravity |
1.33±0.05( spraying)1.33±0.05(dip-spin coating) |
|
4 |
Viscosity |
20-60seconds(spraying) 60-80seconds(dip-spin coating) According to the different configuration of the processing workpiece viscosity |
|
5 |
Operating temperature |
20±2 |
6 Mix Diagram
Caution: Temperature should be controlled in above operation.
7 Coating Process
7.1 Degreasing
The workpiece should be degreased if there is oil on the surface. There are three processing methods:
1.High temperature
2.Neutral water-base degreasing agent
3.Organic solvent such as methylene chloride.
7.2 Derusting
The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.
7.3 Coating
The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.
7.4 Pre-heating
The workpiece after coated should be Pre-heated as soon as possible at 80~150 for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)
7.5 Curing
The workpiece after pre-heating should be cured at 310-350 for 20-40mins. ( according to heat absorption of workpiece.)
8 Attentions
Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.
Avoid irradiation of sunshine and ultraviolet ray for long time