Non-asbestos composite gasket sheet
| Min. Order: | 1000 Kilogram |
|---|---|
| Trade Term: | FOB,CFR,CIF,DDP,EXW |
| Payment Terms: | Paypal, L/C, T/T, WU |
| Supply Ability: | 400ton per month |
| Place of Origin: | Hebei |
Company Profile
| Location: | Hengshui, Hebei, China (Mainland) |
|---|---|
| Business Type: | Manufacturer, Trading Company, Agent, Distributor/Wholesaler, Service, Association |
Product Detail
| Means of Transport: | Ocean, Air, Land |
|---|---|
| Standard or Nonstandard: | Standard |
| Style: | Mechanical Seal |
| Material: | Rubber |
| Brand Name: | bright pearl |
| Production Capacity: | 400ton per month |
| Packing: | in roll or in wooden pallet of about 1000 kgs, 2000kgs net each |
| Delivery Date: | 15 days after received advance payment |
Product Description
Non-asbestos composite gasket sheet
Other name: Non-asbestos composite Gasket Sheet, Non-asbestos composite sheet, Reinforced non-asbestos sheet, Non-asbestos composite beater sheet, Non-asbestos beater sheet.
Manufactured from non-asbestos beater sheet(100% not contain asbestos) with mechanically clinched to 0.18 ~ 0.25mm thick carbon steel tanged (perforated) metal sheet - 08F tinplate insert. It is best gasket material for motorcycle and automobile cylinder head gasket.
This series include:
Reinforced non-asbestos Composite Sheet.
Reinforced non-asbestos Composite Sheet with Both Size Coating Graphite.
Two or more Layers Steel Inserted Reinforced Non-Asbestos Sheet.
Reinforced Non-Asbestos Sheet With Both Size Coating Silicon Resin (anti stick).
Available Size:
Thickness: 1.0mm ~ 3.0mm.
400mm x 1000mm, 500mm x 1000mm, 500mm x 1200mm, 500mm x 1500mm, 510mm x 1016mm, 510mm x 1530mm, 1000mm x 1000mm, 1000mm x 1500mm.
Color: Gray, Black.
The other size is optional or according to the requirements of customers.
Product Date Sheet
| Item | Standard data | |
| Density g/cm³ | 1.3～1.5 | |
| working temperature ℃ | 150～300 | |
| Compressibility % | 10±5 | |
| Recovery ≥ % | 40 | |
| Sealing performance | <0.5cm3/min | |
| causticity | Cusp no rusty | |
| Tensile strength MPa ≥ | 12.7 | |
| Compressive Strength MPa ≥ | 80.0 | |
| Carbon content≥ % | 98 | |
| Ash content ＜% | 1 | |
| With the temperature of 150±2℃, Soaking 20# fluid oil for 5 hours, MPa≥ | oil absorption %≤ | 25 |
| Thickness-increasing %≤ | 0～10 | |
| Stripping performance | No stripe | |
| With the temperature of 15 to 30℃, Soaking 75# kerosene for 5 hours, MPa≥ | oil absorption %≤ | 15 |
| Thickness-increasing %≤ | 0～15 | |
| Stripping performance | No stripe | |
| With the temperature of 100℃, Soaking distilled water for 5 hours, MPa≥ | water absorption %≤ | 15 |
| Thickness-increasing %≤ | 0～15 | |
| Stripping performance | No strip | |