Al2O3 Ceramic Substrates Cellular For Catalytic Converters
| Place of Origin: | Zhejiang |
|---|
Company Profile
| Location: | Shenzhen, Guangdong, China (Mainland) |
|---|---|
| Business Type: | Manufacturer |
| Main Products: | Ceramic Substrates, Honeycomb Ceramic Substrate, Catalytic Converter Substrate |
Product Description
Al2O3 Ceramic Substrates Cellular For Catalytic Converters
Description:
After coated with catalysts, this product is applied in catalytic converter of gasoline vehicle to catalyze, convert and purify the exhaust, making vehicle exhaust reaching standards of Euro IV and Euro V.
Benefits of Products:
Thin wall thickness
Low pressure drop
High surface area
Height compressive strength
Low thermal expansion coefficient
Good thermal impact resistance and thermal shock resistance
Excellent compatibility with various active composition in catalyst
Good performance in cold start, low ignition temperature, quick temperature rise, little air resistance, and high conversion efficiency.
2. 1. Product use
After coated with catalysts, this product is applied in catalytic converter of gasoline vehicle to catalyze, convert and purify the exhaust, making vehicle exhaust reaching standards of Euro IV and Euro V.
2Overall dimensions standards
|
Item |
Standard value |
Tolerance range |
Remark |
|
wall thickness |
0.17MM |
0.03MM 0.02MM |
|
|
density scope |
440g/L |
±60g/L |
|
|
Outside dimension |
≤100MM |
±1MM |
|
|
100MM |
±1% |
|
|
|
Perpendicularity |
≤100MM |
≤1%height |
|
|
Parallelism |
100MM |
≤1%height |
|
Physical and chemical properties
|
Item |
Standard value |
Inspection Method |
|
|
chemical components |
Al2O3 |
35.2±1% |
Chemical analysis |
|
SiO2 |
50.9±1% |
||
|
MgO |
13.9±1% |
||
|
Cordierite Crystal phase |
≥90% |
X-ray diffraction techniques |
|