Custom Lost Wax Carbon Steel Investment Casting Foundry With CNC Machining

Place of Origin: Zhejiang

Company Profile

Location: Suzhou, Jiangsu, China (Mainland)
Business Type: Manufacturer
Main Products: Forged Steel Rings, Forged Rolled Rings, Stainless Steel Forged Rings

Product Detail

Model No.: carbon steel investment casting 009

Product Description

 

Custom Lost Wax Carbon Steel Investment Casting Foundry With CNC Machining

 


 
Quick Detail:

 

1.   A mechanical level made by investment cast process;
2.   Material: SCS13 carbon steel;
3.   Size: 120X150X180mm;
4.   Weight: 0.027kg;
5.   PED and ISO9001:2008 certificated;
6.   Tensile test can be offered;
7.   Low temperature Impact test can be operated.
 
 

Description:


 
Investment casting foundry with OEM casting services for customized parts of stainless steel, carbon steel, duplex alloys, nickel-based materials, and more, with different sizes and configurations: 

 

Stainless Steel (70%)

Carbon Steel (20%)

Alloy Steel (10%)

CF3M (AISI 316L), CF8M (AISI 316), CF8 (AISI 304),CD4MCu, CD4MCuN,ANC20,1.4408,1.4517, 1.4306, 303,  430, 420, 17-4PH, SCS1

and more

SCS16, SCS14, SCS13, 1.0619, WCB, S355JR, 1045 , LCC

and more

ANC2,CLA12C,42CrMo,8Q,4140,6150

and more

 


 
Investment Casting Process:


 
1. TOOL MAKING
A wax injection mold is designed and built to produce castings per customer specifications.
 
2. WAX PRODUCTION
A wax pattern is produced from the wax injection mold.
 
3. PATTERN ASSEMBLY
Wax patterns are attached to gating system by hot knife.
 
4. SHELL MAKING
The pattern assembly is dipped into a ceramic slurry, coated with a refractory material and dried. The process is repeated until the desired thickness and strength is achieved.
 
5. DEWAXING
Using regulated steam pressure, an autoclave melts and remove the wax from the ceramic shells.
 
6.SHELL PREHEAT
High temperature ovens cure and preheat the ceramic shells before pouring.
 
7. CASTING
Pre-heated Ceramic cavities are poured with the molten metal.
 
8.KNOCK OUT
The ceramic shell is removed by vibration knocking and the cluster is cleaned.
 
9.CUT OFF
Castings are cut off from the gating system.
 
10.MACHINING,SURFACE FINISH,AND INSPECTION
After cut off and gate removal, all secondary finishing operations are performed. Each casting is inspected according to customer specifications and requirements.
 
 


Specifications:

 

Standards

ASTM,JIS,DIN,BS,MIL

Maximum Casting Size

500*500*350mm

Casting weight

10g~80kg

Wall thickness

1.5-2mm Min

Casting process type

silica sol lost wax casting

Machining

CNC machining, CNC lathe

Surface finish

electro polishing, satin, hand polished, pickled, zinc plating, vibration polishing;

Tolerances

VDG P690

NDT test

Dye test, X ray test etc

 

 
Competitive Advantage:

 

Precision casting based on the lost wax method is often preferred because:
 
  • complex shapes can be cast as one part without welding
  • products with counter-relief/inner structures can be cast
  • machining costs are reduced to minumum
  • can be performed on almost any alloy.
 