Docmax Medical Latex Glove

20.68~31.88 USD

Location:	Guangzhou, Guangdong, China (Mainland)
Business Type:	Manufacturer
Main Products:	Medical Latex Examination Gloves, Disposable Latex Gloves, OEM Latex Exam Gloves, Nitrile Examination Gloves

Model No.:	DLPMW
Means of Transport:	Ocean, Multimodal Transport, Land
Brand Name:	Docmax
Place of Origin:	Malaysia
Color:	Milky White
Accuracy:	AQL 1.5
Length:	240 mm
Materials:	High-quality Natural Latex
Type:	Lightly Pre-powdered or Powder Free
Size:	XS, S, M, L, XL
Weight of M Size:	5.0 - 6.5g
Surface:	Smooth or Textured
Certification:	CE, ISO, FDA
Production Capacity:	33,280 Carton/Cartons per Month
Packing:	100 pieces/box, 10 boxes/carton, 1600 cartons/20ft container
Delivery Date:	4-5 weeks after the advance payment.

Show

Latex Glove, Disposable LATEX GLOVE, medical latex glove

1) Discription

Name	Medical Latex Examination Gloves
Brand	Docmax
Type	Polymer Coated or Chlorinated Powder Free (sterile or non-sterile).
Material	Top-quality Natural Latex.
Protein Content	Less than 50ug/dm2.
Design & Features	Textured surface, ambidextrous, straight fingers, beaded cuff.
Powder	Free
Storage Conditions	The gloves shall maintain their properties when stored in a dry condition at temperature not higher than 30°C.
Moisture Content	below 0.8% per glove.
Shelf-life	5 years from the date of manufacturing.

2) Quality Standards

Conforms to ASTM D3578, EN455 Part 1 & 2, AQL 1.5. Manufactured under GMP and ISO9001 : 2000 Quality Management System.

Conforms to ASTM D3578, EN455 Part 1 & 2, AQL 1.5.
Manufactured under GMP and ISO9001 : 2000 Quality Management System.

3) Dimensions

Dimensions	Standards
Dimensions	Docmax Gloves	ASTM D3578 (05)
Length (mm)	240 min	220 min (size XS, S) 230 min (size M, L, XL)
Width (mm) • Small • Medium • Large • Extra-large	84 ± 3 94 ± 3 105 ± 3 113 ± 3	80 ± 10 95 ± 10 111 ± 10
Thickness - single wall (mm) • Fingers • Palm	0.12 ± 0.03 0.11 ± 0.03	0.08 min 0.08 min

4) Physical Properties

Property	Meet ASTM D3578 (05)
Elongation at break • Before Aging • After Aging	650% Min 500% Min
Tensile Strength • Before Aging • After Aging	18.0 MPa 14.0 MPa