GCr15 black surface bearing steel
500.0~900.0 USD
| Min. Order: | 1 Metric Ton |
|---|---|
| Trade Term: | FOB |
| Payment Terms: | L/C, T/T, WU |
| Supply Ability: | 3000 Ton/Tons per Month |
| Place of Origin: | Henan |
Company Profile
| Location: | Zhengzhou, Henan, China (Mainland) |
|---|---|
| Business Type: | Manufacturer, Trading Company |
| Main Products: | Drill Pipe, Tinplate, Galvanized Coil, Steel Pipe, Round Steel Bar |
Product Detail
| Model No.: | GCr15 52100 SUJ2 100Cr6 |
|---|---|
| Means of Transport: | Ocean |
| Grade:: | GCr15 52100 SUJ2 100Cr6 534A99 100C6 IIIX15 |
| Standard:: | Other |
| Place of Origin:: | Henan, China (Mainland) |
| Shape: | Bar |
| hot rolled/hot forged:: | black surface/machined surface |
| Application:: | bearing |
| Dimensions:: | 16-800mm |
| Port:: | any port in China |
| Supply Ability: | 3000 Ton/Tons per Month |
| Payment Terms:: | L/C,T/T |
| Production Capacity: | 3000 Ton/Tons per Month |
| Packing: | According to the customer request |
| Delivery Date: | 20-30 days |
Product Description
GCr15 52100 SUJ2 100Cr6 bearing steel
hot rolled and forged or cold drawing
We hope we can providebearing steel round bars with the best price and high quality products for you.
diameter:10-600mm
diameter:10-600mm
hot rolled and forged or cold drawing
Forging:
Forge at 1000°/1050°C.Heat slowly, allowing sufficient time at the forging temperature for the steel to be thoroughly soaked through. Re-heat as often as necessary to keep the temperature above 850°C. After forging cool very slowly, preferably in a furnace.
Annealing:
Heat uniformly to 800°C, equalise, then furnace cool. (Hardness about 229 Brinell).
Stress Relieving:
If machining operations have been heavy or if the tool has an unbalanced section, remove stresses before hardening by heating up to 700°C, equalise, then cool slowly.
Heat uniformly to 800/820°C until heated through. Allow 30 minutes per inch of ruling section and quench immediately in oil.
Tempering:
Heat uniformly and thoroughly at the selected tempering temperatures and hold for at least one hour per inch of total thickness.
Forge at 1000°/1050°C.Heat slowly, allowing sufficient time at the forging temperature for the steel to be thoroughly soaked through. Re-heat as often as necessary to keep the temperature above 850°C. After forging cool very slowly, preferably in a furnace.
Annealing:
Heat uniformly to 800°C, equalise, then furnace cool. (Hardness about 229 Brinell).
Stress Relieving:
If machining operations have been heavy or if the tool has an unbalanced section, remove stresses before hardening by heating up to 700°C, equalise, then cool slowly.
Size: Diameter: 4-800MM length: 2000-5850mm or as customer request in shape ring and bars
Application: Bearing ring, steel rolling mill, machinery, 100Cr6 bearing steel ball is widely used in high-speed and low-noise bearing, bicycle, motorcycle, automobile, bags, electronical
Hardening:Heat uniformly to 800/820°C until heated through. Allow 30 minutes per inch of ruling section and quench immediately in oil.
Tempering:
Heat uniformly and thoroughly at the selected tempering temperatures and hold for at least one hour per inch of total thickness.
Delivery condition:
EAF+LF+VD+(ESR), rolled / forged, annealed / Q+T, black/peeled/turned, UT teste
Delivery time:about 30days
ceritificate
ceritificate
.jpg)