301 stainless steel sheet

Place of Origin: Jiangsu

Company Profile

Location: Wuxi, Jiangsu, China (Mainland)
Business Type: Manufacturer
Main Products: 309s Stainless Steel Sheet, 310s Stainless Steel Sheet, 321 Stainless Steel Sheet, 304 Stainless Steel Sheet

Product Description

301 stainless steel sheet
Quick Details
Grade:
300 Series
Standard:
JIS, AISI, ASTM, GB, DIN, EN
Length:
2000mm-6000mm
Thickness:
0.1mm-120mm
Width:
1000mm-2000mm
Place of Origin:
Wuxi China (Mainland)
Brand Name:
TISCO,JIACO,BISCO,SOUTHWEST,HAOHONGWEIYE STEEL
Model Number:
301 S30100 US301 22Cr17Ni7
Type:
Plate
Application:
Airframe sections Automotive wheel covers Screen frames
Certification:
ISO
surface:
2B/NO.1/NO.4/NO.8/HAIR LINE/MIRROR
standard:
ASTM,AISI,JIS,DON,EN,GB
inspection:
SGS,TPI,buyer's representative
Packaging & Delivery
Packaging Detail:
Export standard package :bundled wooden box or be required; The inner size of container is below: 20 ft GP:5.8m(length)x 2.13m(width)x 2.18m(high) about 24-26 CBM 40 ft GP:11.8m(length)x 2.13m(width)x 2.72m(high)about 68 CBM We will packing as the factory ,and reach the stander of export . Or as the customer request.In addition,We will make the products with good surface protection
Delivery Detail:
regular 15 days after contract date
Specifications
1.manufacturer with competitive price
2.prime quality in international standard
3.sample/MTC available
4.cheaper freight cost
Detail
1. thickness: 0.1mm-120mm
2.width:1000mm-2000mm
3.length:2000mm-6000mm or cut as requirement
4.surface:2B,NO.1,NO.4,NO.8,HAIR LINE
5.standard: ASTM,AISI,JIS,DIN,EN,
  Grade 301 can be supplied with a tensile strength of up to 1800 MPa in strip and wire forms, to produce tempers in the range of 1/16 Hard to Full Hard. The controlled analysis of Grade 301 enables it to retain sufficient ductility in conditions up to 1/2 hard conditions to be roll or brake formed into aircraft, architectural and particularly rail car structural components. However, 3/4 to full hard tempers should be used whenever high wear resistance and spring features are required in components of simple form designs
Grade 301L with low carbon is preferred for improved ductility, and another variant 301LN with higher nitrogen content has a higher work hardening rate than standard 301
Key Properties
The properties for Grade 301 are specified for flat rolled product (plate, sheet and coil) in ASTM A666. Similar but not identical mechanical properties are specified in EN 10088.2 and JIS G4305 and in proprietary specifications.
Composition
Grade
C
Mn
Si
P
S
Cr
Mo
Ni
N
301
ASTM A666
min.
max.
-
0.15
-
2.0
-
1.0
-
0.045
-
0.030
16.0
18.0
-
6.0
8.0
-
0.10
301L
JIS G4305
min.
max.
-
0.03
-
2.0
-
1.0
-
0.045
-
0.030
16.0
18.0
-
6.0
8.0
-
0.20
1.4318/301LN
EN 10088-2
min.
max.
-
0.03
-
2.0
-
1.0
-
0.045
-
0.015
16.5
18.5
-
6.0
8.0
0.10
0.20
Mechanical Properties
Grade 301 Temper ASTM A666
Tensile Strength (MPa) min.
Yield Strength 0.2% Proof (MPa) min.
Elongation (% in 50mm) (thick.>0.76mm) min.
Bend Test (thickness > 1.27mm)
Bend Angle (°)
Factor
Annealed
515
205
40
-
-
1/16 Hard
620
310
40
180
1
1/8 Hard
690
380
40
180
1
1/4 Hard
860
515
25
90
2
1/2 Hard
1035
760
18
90
2
3/4 Hard
1205
930
12
90
3
Full Hard
1275
965
9
90
5
Bend test is around a diameter of the Bend Factor multiplied by the steel thickness.
Physical Properties
Grade
Density (kg/m3)
Elastic Modulus (GPa)
Mean Coefficient of Thermal Expansion (mm/m/°C)
Thermal Conductivity (W/m.K)
Specific Heat 0-100°C
(J/kg.K)
Electrical Resistivity (nW.m)
0-100°C
0-315°C
0-538°C
at 100°C
at 500°C
301
8000
193
17.0
17.2
18.2
16.2
21.5
500
720
Corrosion Resistance
Corrosion resistance is similar to that of 304. Good resistance in applications involving external exposure to mildly corrosive conditions at ambient temperatures.
Heat Resistance
Good oxidation resistance in intermittent service to 840°C and in continuous service to 900°C, although not usually chosen for this environment.
Heat Treatment
Solution Treatment (Annealing) - Heat to 1010-1120°C and cool rapidly. Use low side of range for intermediate annealing. This grade cannot be hardened by thermal treatment.
Cold Working
Grade 301 and its low carbon variants are used where a high strength stainless steel is required. The grades work harden at the very high rate of approximately 14MPa/%Ra (14MPa increase in tensile strength for each 1% reduction of area of cold work), resulting in high achievable strengths from cold rolling and from roll forming. The strain-hardened austenite is at least partially transformed to martensite by this work. Despite the high strengths achieved there is still enough residual ductility to enable severe cold deformation. Although non-magnetic in the annealed condition, when cold worked the grade becomes strongly attracted to a magnet.
Welding
Good characteristics suited to all standard methods. Grade 308L filler rod is recommended. Welds in Grade 301 must be annealed for maximum corrosion resistance; this is not necessary in 301L or 301LN. Welding and post weld annealing will both remove high strength induced by prior cold rolling.
Spot welding is commonly used to assemble cold rolled 301 components. The very small heat affected zone associated with this rapid welding technique results in little reduction of overall component strength.
Applications
Typical applications include:
•         Rail car structural components - often roll formed, brake pressed or stretch formed to profiles but also used flat.
•         Airframe sections
•         Highway trailer components
•         Automotive wheel covers
•         Wiper blade holders and clips
•         Toaster springs
•         Stove element clips
•         Screen frames
•         Curtain walls