dual wall tubing
| Place of Origin: | Jiangsu |
|---|
Company Profile
| Location: | Suzhou, Jiangsu, China (Mainland) |
|---|---|
| Business Type: | Manufacturer, Trading Company, Service |
| Main Products: | Tubing, Single Wall Tubing, Dual Wall Tubing |
Product Description
Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing (3X) Description: Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing Adhesive lined heat shrink tubing with environmental sealing capability for a wide variety of electrical applications, including automotive and marine wire harness, wire splices, breakouts, and connector-to- cable transitions. Features 1.3:1 shrink ratio 2.Longitudinal shrink ratio: ≤+8% 3.Out jacket flame retardant, inner adhesive self-extinguished 4.Super sealing against water, moisture or other contaminants 5.Continuous operating temperature: -55℃~ 125℃ 6.Shrink temperature: 120℃ |
Size | As supplied | After recovery (mm) | Standard Package | |||
Inch | mm | Internal Diameter(mm) | Internal Diameter | Total Wall Thickness | Wall Thickness of Adhesive | m/spool |
1/8 | 3.2 | 3.2 | 1.0 | 0.90±0.15 | 0.35±0.10 | 200 |
3/16 | 4.8 | 4.8 | 1.6 | 1.00±0.15 | 0.40±0.10 | 100 |
1/4 | 6.4 | 6.4 | 2.20 | 1.25±0.15 | 0.45±0.12 | 100 |
5/16 | 7.9 | 7.9 | 2.70 | 1.30±0.15 | 0.50±0.12 | 100 |
3/8 | 9.5 | 9.5 | 3.20 | 1.40±0.15 | 0.50±0.12 | 50 |
1/2 | 12.7 | 12.7 | 4.20 | 1.70±0.15 | 0.50±0.12 | 36.6 |
5/8 | 15.0 | 15.0 | 5.20 | 1.80±0.15 | 0.55±0.15 | 30.5 |
3/4 | 19.1 | 19.1 | 6.30 | 1.95±0.15 | 0.55±0.15 | 30.5 |
1 | 25.4 | 25.4 | 8.50 | 2.05±0.20 | 0.55±0.15 | 30.5 |
1- 1/4 | 30.0 | 30.0 | 10.20 | 2.20±0.20 | 0.60±0.15 | 24.4 |
1- 1/2 | 39.0 | 39.0 | 13.50 | 2.50±0.20 | 0.60±0.15 | 18.3 |
2 | 50.0 | 50.0 | 17.00 | 2.80±0.25 | 0.70±0.15 | 12.2 |
5/2 | 64 | 64 | 21.00 | 3.00±0.25 | 0.70±0.15 | 6.1 |
3 | 75 | 75 | 25.00 | 3.00±0.30 | 1.00±0.20 | 1.22 |
7/2 | 90 | 90 | 30.00 | 3.00±0.30 | 1.00±0.20 | 1.22 |
4 | 100 | 100 | 34.00 | 3.00±0.30 | 1.00±0.20 | 1.22 |
5 | 125 | 125 | 42.00 | 3.00±0.30 | 1.00±0.20 | 1.22 |
Technical Data:
Test Item | Test Method | Test Result |
Tensile Strength(Mpa) | ASTM D2671 | ≥10.4 |
Elongation% | ASTM D2671 | ≥300 |
Tensile Strength after-aging (Mpa) | UL 224 158×168hr | ≥7.3 |
Elongation after Aging% | UL 224 158℃×168hr | ≥200 |
Dielectric Strength | IEC 243 | ≥ 15 |
Volume Resistance(Ω.cm) | ASTM D876 | ≥ 1014Ω.cm |
Hot Melting Adhesive Property
Test Item | Test Method | Test Result |
Water absorption ratio: | ASTM-D570 | <0.2% |
Softing point | ASTM-E8 | 95℃ |
Strength of pearing(PE) | ASTM-D1000 | 120N/25m |
Strength of pearing(AL) | ASTM-D1000 | 80N/25m |
.gif)