1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | ||
Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Maximal Temperature (°C) | 650 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity 20°C (10-6ohm*m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal conductivity (KJ/m*h*°C) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
Extend strength (a*10-6/°C) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Melting point ( °C) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength(N/mm2) | 588-735 | 630-780 | 637-780 | 630-780 | 637-784 | 650-800 | 680-830 | |
Extension rate% | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Section shrink rate (%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Repeatedly bending frequency (F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Specific heat J/g. | 0.49 | 0.494 | 0.52 | 0.46 | 0.49 | 0.494 | 0.494 | |
Linear expansion coefficient a×10-6/201000 | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
hardness (H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Rapid life h/ | ≥80/1250 | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1350 | ≥80/1350 | ||
Microstructure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetism | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |