430 Stainless Steel Sheet/Stainless Steel 430 Sheet/430 SS Sheet

Like other straight chromium grades, Type Stainless Steel 430 Sheet annealed is subject to stretcher strains. Skin of Stainless Steel 430 Sheet passing following annealing greatly reduces this possibility although this reduces ductility somewhat. Likewise a condition akin to stretcher strains may sometimes develop during deep drawing known as roping. The roping of Stainless Steel 430 Sheet is characterized by the appearance of shallow ridges and valleys in the side walls and caused by excessive stretching.

Typical properties in the annealed condition

The properties quoted in this publication are typical of mill product and unless indicated should not be regarded as guaranteed minimum values for design purposes. For these purposes refer to the relevant specification.
2.The information of Stainless Steel 430 Sheet:

1.Superiority	High quality and Competitive price
2. Third part inspection	Third part inspection is supported by us
3. Application	construction field, ships building industry, petroleum & chemical industries, war and electricity industries, food processing and medical industry, boiler heat exchanger, machinery and hardware fields, etc.
4. Packing	export standard or as customers' requirement
5. Delivery time	Within 10 days after the advance payment if there are no special requires
6. Payment terms	30% TT in advance, 70%TT after the copy of BL OR 30% TT in advance, 70% LC at sight.
7. Attention	we will supply you good quality and bottom price and first-class service in china and hope to be your golden supplier.

Other relations of Stainless Steel 430 Sheet:
1. Mechanical properties at room temperature  

	Typical	Minimum
Tensile Strength, MPa	530	450
Proof Strength, 0.2 % , MPa	360	205
Elongation (Percent in Lo=5.65 So) MPa	25	22
Hardness	160	-

2. Properties at elevated temperatures

Short time elevated temperature tensile strength

Creep data

Stress for a creep rate of 1% in 10 000 h

Recommended maximum service temperature

(Oxidising Conditions)

Continuous Service            750 oC Intermittent Service             850 oC

Note: Service in the temperature range 425 -525 oC for over 100 hours will cause the steel to be brittle on cooling to room temperature.

Contact Supplier