electrical galvanized prestressed concrete wire
| Min. Order: | 5 Metric Ton |
|---|---|
| Payment Terms: | L/C, D/A, T/T |
| Supply Ability: | 4000mt/month |
| Place of Origin: | Henan |
Company Profile
| Location: | China (Mainland) |
|---|---|
| Business Type: | Manufacturer |
| Main Products: | Industrial Aluminum Coil;indrstrial Aluminum Sheet; Industrial Aluminum Sheet; Industrial Aluminum Plate, Hydrophilic Aluminum Foil;aluminum Foil; Aluminum Foil For Capacitor, Aluminum Foil;hydrophilic Aluminum Foil;aluminum Foil For Capacitor, Embossed Aluminum Sheets For Furniture/refrigerator/decoration, Aluminum Foil;aluminum Foils For Packing;aluminum Foils For Capacitor;packing Used Aluminum Foils |
Product Detail
| Model No.: | summary |
|---|---|
| Means of Transport: | Ocean |
| size: | 4.00-12.00mm |
| tensile strength: | 1460-1860mpa |
| Production Capacity: | 4000mt/month |
| Packing: | according to customers requirement |
| Delivery Date: | 2 or 3 weeks after the confirmation of teh order |
Product Description
Ele-galvanized pc wire
Specification
1.Size:4.00mm-7.50mm
2.Tensile strength 1370-1860MPA
3.Standard:GB/T5223-2002, ASTMA421, ASTMA648, BS5896-80, JISG3536 or according to customers' requirements.
2.Tensile strength 1370-1860MPA
3.Standard:GB/T5223-2002, ASTMA421, ASTMA648, BS5896-80, JISG3536 or according to customers' requirements.
4.low-relaxation 1000hrs test passed
5 Application: non-concrete used in mining ,cable support .plug-ins such as cable-stayed and highways barriers.
6 Packing :Lining is water-proof plastic, outer layer is polypropylene woven bag on wood pallet or wood spool and according to customers' requirements.
6Advantages
a) Large difference in coating thickness: Electricity galvanized coating thickness average in 70-150g/m2, hot zinc coating thickness is generally about 300g/m2
b )Electricity galvanized has better bonding and surface condition .
c )Electricity galvanized by erosion slower
Size/mm | Nominal Tensile Strength/Mpa | Yield Strength/Mpa | Elongation Lo=200mm/% | 180oBending Times | Relaxation | ||
Times | Bending Radius/mm | Condition | % | ||||
4.00 | 1470 1570 1670 1770 1860 | 1290 1380 1470 1560 1640 | ≥3.5 | ≥3 | 10 | Initial load being 70% of nominal breaking strength | ≤2.5 |
4.80 | ≥4 | 15 | |||||
5.00 | |||||||
5.25 | |||||||
6.00 | |||||||
6.25 | 20 | ||||||
7.00 | |||||||