High silica fiberglass filter mesh

NINGXIN refractory cloth filters are designed to extract dross, slag, refractory particles, and non-metallic inclusions from molten metals.

NINGXIN cloth filters were developed as a low cost,high efficiency alternative to cellular ceramic and reticulated ceramic foam filtration systems.Made from specially treated silica fibers,cloth filters are capable of withstanding pouring temperatures ranging up to 1750°C.

NINGXIN cloth filters are ideal for inmold filtration of gray, malleable, white, compacted graphite,and ductile cast irons, as well as non-ferrousaluminum and copper-based metal alloys.

The filters are available in a choice of mesh sizes, and can be cut or formed to virtually any desired size or shape.

For steel casting
Work temperature 1600-1650(℃)
Softening rate 1750(℃)
Lasting working time ≤15seconds
The tensile strength of normal atmospheric temperature  ≥16kg/4
Emit the quantity of gas  ≤60cm3/g
Density 580g/m2
Hole Size 1.5x1.5mm/2.0x2.0mm/2.5x2.5mm
Weave pattern Leno
%open 50-60%

For steel casting cap style
For iron casting
Work temperature 1400-1450(℃)
Softening rate 1750(℃)
Lasting working time ≤10 seconds
The tensile strength of normal atmospheric temperature  ≥8kg/4
Emit the quantity of gas  ≤60cm3/g
Density 195g/m2
Hole Size 1.5x1.5mm/2.0x2.0mm/2.5x2.5mm
Weave pattern Leno
%open 50-60%

For aluminium casting
Work temperature 850(℃)
Softening rate 1200(℃)
Lasting working time ≤10seconds
The tensile strength of normal atmospheric temperature  ≥6kg/4
Emit the quantity of gas  ≤30cm3/g
Density 300g/m2
Hole Size 1.2x1.2mm/1.5x1.5mm/2.0x2.0mm
Weave pattern Leno
%open 50-60%

Contact Supplier