INCOLOY901 STRIP PLATE SHEET
Incoloy 901 Strip plate sheet is a nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A substantial iron content enables the alloy to combine high strength with good forging characteristics.
Incoloy 901 wire has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.
To ensure the quality of our product, we can produce the product with raw materials from the international suppliers. Every batch of product can be tracked to the original raw material supplier. We co-operate with international suppliers like Allvac(ATI), Bohler, Carpenter, Dunkirk, Gloria, OttoKumpu, SMC, ThyssenKrupp VDM, Valbruna, etc.
Sheet Plate Strip: Thickness:0.05mm above
Chemical composition(%) of Incoloy 901 Strip:
Alloy | Ni | Cr | Fe | C | Mn | Si | Mo | Al | Ti | B |
Incoloy 825 | balance | 12.5 | 34.0 | 0.05 | 0.24 | 0.12 | 6.0 | 0.15 | 2.7 | |
0.015 |
Mechanical Properties of Incoloy 901 Strip:
Test Temperature | 0.2% Offset Yield Strength | Ultimate Tensile Strength | % Elongation in 2" | % Reduction of Area |
°F | °C | ksi | MPa | ksi | MPa |
70 800 1000 1200 1300 1400 1500 | 21.1 427 538 649 704 760 816 | 125.0 116.5 113 117 114 102.5 79 | 862 803 779 807 786 707 545 | 175 159 156 150 130 107.5 81 | 1207 1096 1076 1034 896 741 559 | 15.0 16.0 17.0 14.0 11.5 9.0 13.0 | 19.0 25.5 29.0 21.0 15.5 14.5 20.0 |
Workability:
1. Hot Working:
Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.
2. Weldability:
Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.
Applications:
Gas turbine engine discs, shafts, rings, casings and seals.
Product Description: The product produced by us is of good quality and is priced reasonably.
Competitive price: The labour cost and cost on procuring the raw materials is low and hence the manufacturing cost is reasonable. We provide high facility in short producing cycle and have strong adaptive capacity in producing variation of products.
High quality assured: The work done by us has a good command of advanced technological process in the respect of smelting, rolling, drawing and heat treatment up to finished products. The chemical analysis department, the physical testing department and the quality control department all operate an all-round monitoring of our products from raw materials to final products.
Packing Process & Transportation:
Packaging: Seal up, with plastic inside and wooden case or carton outside; or according to the customer's requirements.
Transportation: By air: Beijing International Airport OR By sea: Trianjin Seaport
We provide our customers with excellent services. If you want more detailed information of this product or related problems, please contact with us, we will reply as soon as possible (general in 24 hours).