extrusion & injection grade HDPE
950.0~1150.0 USD
| Min. Order: | 5 Ton |
|---|---|
| Trade Term: | FOB |
| Payment Terms: | L/C, D/P, D/A, T/T, WU |
| Supply Ability: | 4000 ton per month |
| Place of Origin: | Liaoning |
Company Profile
| Location: | Hefei, Anhui, China (Mainland) |
|---|---|
| Business Type: | Manufacturer, Trading Company, Agent, Distributor/Wholesaler, Other |
| Main Products: | Magnesium Ingot Magnesium Alloy Ingot |
Product Detail
| Model No.: | extrusion grade , injection grade |
|---|---|
| Means of Transport: | Ocean, Air, Land |
| Classification: | Others |
| Brand Name: | jc |
| CAS No.: | 9002-88-4 |
| Purity: | 100% |
| specific gravity: | 0.941~0.960 |
| melting point: | 142℃ |
| decomposition temperature: | 300℃ |
| relative density: | 0.941-0.960 |
| density: | 0.940-0.976 g/cm3 |
| Production Capacity: | 4000 ton per month |
| Packing: | 25kg a bag, 18 ton a 20'fcl , |
| Delivery Date: | 10 days |
Product Description
Extrusion & injection grade HDPE
HDPE:
HDPE cable material Property | Unit | Typical Value |
Mass density | g/cm 3 | 0.941-0.959 |
Melt flow Rate(190 centidegree /2.16kg) | g/10min | ≤1.0 |
Tensile yield strength | MPa | ≥19.0 |
Flexural modulus | Mpa | ≥965 |
Elongation@ break | % | ≥400 |
Impact Embrittlement temperature | centidegree | MAX -118 |
Dielectric Constant | 100KHZ | 2.32 |
1MHZ | 2.31 | |
Loss Tangent | 100KHZ | MAX 0.0001 |
1MHZ | MAX 0.0001 | |
Volume resistivity | OHM-CM | MIN 1x10 15 |
Application | Mainly used for the production of high toughness of the telephone,cable insulation material | |
LDPE:
Physical Properties | Test Method | Nominal Value | Unit | |
Density | ISO 1183 | 0.921 | g/cm3 | |
Melt Mass-Flow Rate (MFR) | ISO 1133 | 1.9 | g/10min | |
Hardness | ||||
Shore Hardness (shore D) | ISO 868 | 45 | ||
Mechanical Properties | ||||
Tensile Modulus | ISO 527-2 | 175 | MPa | |
Tensile Strength | Yield, | ISO 527-2 | 9.0 | MPa |
Break, | 13.0 | MPa | ||
Tensile Strain(Break) | ISO 527-2 | 850 | % | |
Modulus of Elasticity | Internal Method | 250 | MPa | |
Thermal | ||||
Vicat Softening Temperature | ISO 306/A50 | 89.0 | °C | |
Melting Temperature (DSC) | DIN 53765 | 108 | °C | |
Peak Crystallization Temperature (DSC) | DIN 53765 | 97.0 | °C | |
Heat of Fusion | DIN 53765 | 110 | J/g | |
Electrical | ||||
Volume Resistivity | ASTM D257 | 8.5E+15 | ohm •cm | |
Dielectric Strength | ASTM D149 | 30.0 | kV/mm | |
Dielectric Constant (60Hz) | ASTM D150 | 2.20 | % | |
Dissipation Factor (60 Hz) | ASTM D150 | 0.00050 | ||
LLDPE
Properties | Test conditon | Test method | Test data | Unit |
Density | 0.91 | |||
MFI | 2 | |||
Drop impact strength | ASTM D-1709 | 90 | g | |
Elongation ,vertical/horizontal | ASTM D-882 | 600/800 | % | |
tensilestrength,thermal resistance | ASTM D-1004 | 105/95 | Kg/cm | |
elongation | ASTM D-638 | 930 | % | |
tensile strength | ASTM D-638 | 180 | ||
tensile strength,vertical/horizontal | ASTM D-882 | 380/350 | ||
Vicat softening point | ASTM D-1525 | 103 | °C | |
melting point | ASTM D-2117 | 126 | °C | |
Turbidity | ASTM D-1009 | 12 | % | |
45 glossness | ASTM D-2457 | 75 | % | |
HDPE Raw Material,HDPE virgin granules
HDPE resins are produced with low pressure gas phase process. The products are primarily used for extrusion application such as flat Yarn, coarse monofilament, film & sheets and injection molding such as pallets, crates, bottle caps and industrial containers